PBT 1731 物性表资料
PBT材料的其他牌号：
S650FR BK851
PBT 420se0
PBT r48
PBT 830
PBT 420
PBT 815
PBT 357u
PBT dr51
PBT 364
PBT 1731
PBT 325
加工方法 | · 注射成型 | ||||||||||||||||
多点数据 | · Coefficient of Thermal Expansion vs. Temperature (ASTM E831) · Elastic Modulus vs Temperature (ASTM D4065) · Flexural DMA (ASTM D4065) · Instrumented Impact (Energy) (ASTM D3763) · Instrumented Impact (Load) (ASTM D3763) · Pressure-Volume-Temperature (PVT - Zoller Method) · Shear DMA (ASTM D4065) · Specific Heat vs. Temperature (ASTM D3417) · Tensile Fatigue · Tensile Stress vs. Strain (ASTM D638) · Thermal Conductivity vs. Temperature (ASTM E1530) · Viscosity vs. Shear Rate (ASTM D3835) | ||||||||||||||||
物理性能 | 额定值 | 单位制 | 测试方法 | ||||||||||||||
比重 | 1.22 | g/cm3 | ASTM D792, ISO 1183 | ||||||||||||||
特定体积 | 0.820 | cm3/g | ASTM D792 | ||||||||||||||
熔流率 | |||||||||||||||||
250°C/5.0 kg | 9.6 | g/10 min | ASTM D1238 | ||||||||||||||
250°C/5.0 kg | 8.0 | g/10 min | ISO 1133 | ||||||||||||||
收缩率 | Internal Method | ||||||||||||||||
流动: 3.20 mm | 0.50 到 0.70 | % | |||||||||||||||
横向流动: 3.20 mm | 0.60 到 0.80 | % | |||||||||||||||
吸水率 | ISO 62 | ||||||||||||||||
饱和, 23°C | 0.28 | % | |||||||||||||||
平衡, 23°C, 50% RH | 0.080 | % | |||||||||||||||
机械性能 | 额定值 | 单位制 | 测试方法 | ||||||||||||||
拉伸模量 | |||||||||||||||||
-- 3 | 2370 | MPa | ASTM D638 | ||||||||||||||
-- | 2330 | MPa | ISO 527-2/1 | ||||||||||||||
抗张强度 | |||||||||||||||||
屈服 4 | 61.4 | MPa | ASTM D638 | ||||||||||||||
屈服 | 60.0 | MPa | ISO 527-2/50 | ||||||||||||||
断裂 4 | 56.0 | MPa | ASTM D638 | ||||||||||||||
断裂 | 58.0 | MPa | ISO 527-2/50 | ||||||||||||||
伸长率 | |||||||||||||||||
屈服 4 | 5.0 | % | ASTM D638 | ||||||||||||||
屈服 | 5.0 | % | ISO 527-2/50 | ||||||||||||||
断裂 4 | 100 | % | ASTM D638 | ||||||||||||||
断裂 | 90 | % | ISO 527-2/50 | ||||||||||||||
弯曲模量 | |||||||||||||||||
50.0 mm 跨距 5 | 2340 | MPa | ASTM D790 | ||||||||||||||
-- 6 | 2210 | MPa | ISO 178 | ||||||||||||||
弯曲强度 | |||||||||||||||||
-- 6, 7 | 93.0 | MPa | ISO 178 | ||||||||||||||
屈服, 50.0 mm 跨距 5 | 93.1 | MPa | ASTM D790 | ||||||||||||||
冲击性能 | 额定值 | 单位制 | 测试方法 | ||||||||||||||
简支梁缺口冲击强度 8 (23°C) | 65 | kJ/m2 | ISO 179/1eA | ||||||||||||||
悬壁梁缺口冲击强度 | |||||||||||||||||
-30°C | 110 | J/m | ASTM D256 | ||||||||||||||
23°C | 670 | J/m | ASTM D256 | ||||||||||||||
23°C, 6.40 mm | 160 | J/m | ASTM D256 | ||||||||||||||
-30°C 9 | 16 | kJ/m2 | ISO 180/1A | ||||||||||||||
23°C 9 | 59 | kJ/m2 | ISO 180/1A | ||||||||||||||
装有测量仪表的落镖冲击 | ASTM D3763 | ||||||||||||||||
-30°C, Total Energy | 61.5 | J | |||||||||||||||
23°C, Total Energy | 61.1 | J | |||||||||||||||
热性能 | 额定值 | 单位制 | 测试方法 | ||||||||||||||
热变形温度 | |||||||||||||||||
0.45 MPa, 未退火, 6.40 mm | 116 | °C | ASTM D648 | ||||||||||||||
1.8 MPa, 未退火, 3.20 mm | 93.0 | °C | ASTM D648 | ||||||||||||||
1.8 MPa, 未退火, 6.40 mm | 107 | °C | ASTM D648 | ||||||||||||||
1.8 MPa, 未退火, 64.0 mm 跨距 10 | 99.0 | °C | ISO 75-2/Af | ||||||||||||||
维卡软化温度 | |||||||||||||||||
-- | 125 | °C | ASTM D1525 11 | ||||||||||||||
-- | 127 | °C | ISO 306/B50 | ||||||||||||||
-- | 130 | °C | ISO 306/B120 | ||||||||||||||
线形膨胀系数 | |||||||||||||||||
流动: -40 到 40°C | 0.000078 | cm/cm/°C | ASTM E831, ISO 11359-2 | ||||||||||||||
流动: -40 到 95°C | 0.000083 | cm/cm/°C | ASTM E831 | ||||||||||||||
横向: -40 到 40°C | 0.000076 | cm/cm/°C | ASTM E831, ISO 11359-2 | ||||||||||||||
RTI Elec | 75.0 | °C | UL 746 | ||||||||||||||
RTI Imp | 75.0 | °C | UL 746 | ||||||||||||||
RTI Str | 75.0 | °C | UL 746 | ||||||||||||||
电气性能 | 额定值 | 测试方法 | |||||||||||||||
耐电弧性 12 | PLC 5 | ASTM D495 | |||||||||||||||
相比耐漏电起痕指数(CTI) | PLC 2 | UL 746 | |||||||||||||||
高电弧燃烧指数(HAI) | PLC 0 | UL 746 | |||||||||||||||
高电压电弧起痕速率 (HVTR) | PLC 2 | UL 746 | |||||||||||||||
热丝引燃 (HWI) | PLC 2 | UL 746 | |||||||||||||||
可燃性 | 额定值 | 测试方法 | |||||||||||||||
UL 阻燃等级 (1.50 mm) | HB | UL 94 | |||||||||||||||
注射 | 额定值 | 单位制 | |||||||||||||||
干燥温度 | 110 | °C | |||||||||||||||
干燥时间 | 4.0 到 6.0 | hr | |||||||||||||||
干燥时间，最大 | 8.0 | hr | |||||||||||||||
建议的最大水分含量 | 0.020 | % | |||||||||||||||
建议注入量 | 50 到 80 | % | |||||||||||||||
螺筒后部温度 | 243 到 266 | °C | |||||||||||||||
螺筒中部温度 | 249 到 271 | °C | |||||||||||||||
螺筒前部温度 | 254 到 277 | °C | |||||||||||||||
射嘴温度 | 254 到 271 | °C | |||||||||||||||
加工（熔体）温度 | 260 到 277 | °C | |||||||||||||||
模具温度 | 65.6 到 87.8 | °C | |||||||||||||||
背压 | 0.345 到 0.689 | MPa | |||||||||||||||
螺杆转速 | 50 到 80 | rpm | |||||||||||||||
排气孔深度 | 0.013 到 0.020 | mm | |||||||||||||||