PPO N190X物性表资料
PPO材料的其他牌号：
PPO GFN2
PPO N190X
PPO GFN3
PPO N750
PPO N850
PPO V0150B
PPO GFN1720
PPO PX1390
加工方法 | · 注射成型 | |||||||||||||||||
多点数据 | · Coefficient of Thermal Expansion vs. Temperature (ASTM E831) · Elastic Modulus vs Temperature (ASTM D4065) · Flexural DMA (ASTM D4065) · Instrumented Impact (Energy) (ASTM D3763) · Instrumented Impact (Load) (ASTM D3763) · Pressure-Volume-Temperature (PVT - Zoller Method) · Shear DMA (ASTM D4065) · Specific Heat vs. Temperature (ASTM D3417) · Tensile Creep (ASTM D2990) · Tensile Fatigue · Tensile Stress vs. Strain (ASTM D638) · Thermal Conductivity vs. Temperature (ASTM E1530) · Viscosity vs. Shear Rate (ASTM D3835) | |||||||||||||||||
物理性能 | 额定值 | 单位制 | 测试方法 | |||||||||||||||
比重 | 1.13 | g/cm3 | ASTM D792 | |||||||||||||||
熔流率 (280°C/5.0 kg) | 20 | g/10 min | ASTM D1238 | |||||||||||||||
溶化体积流率（MVR） (280°C/5.0 kg) | 23.0 | cm3/10min | ISO 1133 | |||||||||||||||
收缩率 - 流动 (3.20 mm) | 0.50 到 0.70 | % | Internal Method | |||||||||||||||
吸水率 (24 hr) | 0.080 | % | ASTM D570 | |||||||||||||||
室外适用性 | f1 | UL 746C | ||||||||||||||||
硬度 | 额定值 | 单位制 | 测试方法 | |||||||||||||||
洛氏硬度 (R 计秤) | 120 | ASTM D785 | ||||||||||||||||
机械性能 | 额定值 | 单位制 | 测试方法 | |||||||||||||||
拉伸模量 | ||||||||||||||||||
-- 3 | 2580 | MPa | ASTM D638 | |||||||||||||||
-- | 2600 | MPa | ISO 527-2/1 | |||||||||||||||
抗张强度 | ||||||||||||||||||
屈服 4 | 60.7 | MPa | ASTM D638 | |||||||||||||||
屈服 | 58.0 | MPa | ISO 527-2/50 | |||||||||||||||
断裂 4 | 47.6 | MPa | ASTM D638 | |||||||||||||||
断裂 | 50.0 | MPa | ISO 527-2/50 | |||||||||||||||
伸长率 | ||||||||||||||||||
屈服 4 | 3.6 | % | ASTM D638 | |||||||||||||||
屈服 | 3.2 | % | ISO 527-2/50 | |||||||||||||||
断裂 4 | 9.0 | % | ASTM D638 | |||||||||||||||
断裂 | 9.2 | % | ISO 527-2/50 | |||||||||||||||
弯曲模量 | ||||||||||||||||||
50.0 mm 跨距 5 | 2500 | MPa | ASTM D790 | |||||||||||||||
100 mm 跨距 6 | 2300 | MPa | ASTM D790 | |||||||||||||||
-- 7 | 2350 | MPa | ISO 178 | |||||||||||||||
弯曲强度 | ||||||||||||||||||
-- 7, 8 | 87.0 | MPa | ISO 178 | |||||||||||||||
屈服, 50.0 mm 跨距 5 | 98.0 | MPa | ASTM D790 | |||||||||||||||
屈服, 100 mm 跨距 6 | 91.4 | MPa | ASTM D790 | |||||||||||||||
抗泰伯磨耗 (1000 Cycles, 1000 g, CS-17 转轮) | 76.0 | mg | ASTM D1044 | |||||||||||||||
冲击性能 | 额定值 | 单位制 | 测试方法 | |||||||||||||||
简支梁缺口冲击强度 (23°C) | 20 | kJ/m2 | ISO 179/2C | |||||||||||||||
悬壁梁缺口冲击强度 | ||||||||||||||||||
-30°C | 100 | J/m | ASTM D256 | |||||||||||||||
23°C | 290 | J/m | ASTM D256 | |||||||||||||||
23°C 9 | 20 | kJ/m2 | ISO 180/1A | |||||||||||||||
无缺口悬臂梁冲击 (23°C) | 720 | J/m | ASTM D4812 | |||||||||||||||
装有测量仪表的落镖冲击 (23°C, Total Energy) | 50.0 | J | ASTM D3763 | |||||||||||||||
热性能 | 额定值 | 单位制 | 测试方法 | |||||||||||||||
热变形温度 | ||||||||||||||||||
0.45 MPa, 未退火, 3.20 mm | 95.0 | °C | ASTM D648 | |||||||||||||||
0.45 MPa, 未退火, 64.0 mm 跨距 10 | 95.0 | °C | ISO 75-2/Bf | |||||||||||||||
1.8 MPa, 未退火, 3.20 mm | 78.0 | °C | ASTM D648 | |||||||||||||||
1.8 MPa, 未退火, 6.40 mm | 86.0 | °C | ASTM D648 | |||||||||||||||
1.8 MPa, 未退火, 64.0 mm 跨距 10 | 82.0 | °C | ISO 75-2/Af | |||||||||||||||
维卡软化温度 | ||||||||||||||||||
-- | 104 | °C | ASTM D1525 11 | |||||||||||||||
-- | 107 | °C | ISO 306/B120 | |||||||||||||||
线形膨胀系数 | ASTM E831 | |||||||||||||||||
流动: -40 到 40°C | 0.000077 | cm/cm/°C | ||||||||||||||||
横向: -40 到 40°C | 0.000081 | cm/cm/°C | ||||||||||||||||
导热系数 | 0.24 | W/m/K | ASTM C177 | |||||||||||||||
RTI Elec | 95.0 | °C | UL 746 | |||||||||||||||
RTI Imp | 80.0 | °C | UL 746 | |||||||||||||||
RTI Str | 95.0 | °C | UL 746 | |||||||||||||||
电气性能 | 额定值 | 单位制 | 测试方法 | |||||||||||||||
体积电阻率 | 1.8E+16 | ohm·cm | ASTM D257 | |||||||||||||||
介电强度 (3.20 mm, in Oil) | 19 | kV/mm | ASTM D149 | |||||||||||||||
介电常数 | ASTM D150 | |||||||||||||||||
100 Hz | 2.74 | |||||||||||||||||
100 kHz | 2.60 | |||||||||||||||||
耗散因数 | ASTM D150 | |||||||||||||||||
100 Hz | 0.013 | |||||||||||||||||
100 kHz | 0.0055 | |||||||||||||||||
耐电弧性 12 | PLC 7 | ASTM D495 | ||||||||||||||||
相比耐漏电起痕指数(CTI) | PLC 1 | UL 746 | ||||||||||||||||
高电弧燃烧指数(HAI) | PLC 2 | UL 746 | ||||||||||||||||
高电压电弧起痕速率 (HVTR) | PLC 4 | UL 746 | ||||||||||||||||
热丝引燃 (HWI) | PLC 2 | UL 746 | ||||||||||||||||
可燃性 | 额定值 | 单位制 | 测试方法 | |||||||||||||||
UL 阻燃等级 | UL 94 | |||||||||||||||||
1.02 mm | HB | |||||||||||||||||
1.47 mm | V-0 | |||||||||||||||||
3.00 mm | 5VA | |||||||||||||||||
极限氧指数 | 39 | % | ASTM D2863 | |||||||||||||||
注射 | 额定值 | 单位制 | ||||||||||||||||
干燥温度 | 76.7 到 82.2 | °C | ||||||||||||||||
干燥时间 | 3.0 到 4.0 | hr | ||||||||||||||||
干燥时间，最大 | 8.0 | hr | ||||||||||||||||
建议的最大水分含量 | 0.020 | % | ||||||||||||||||
建议注入量 | 30 到 70 | % | ||||||||||||||||
螺筒后部温度 | 216 到 266 | °C | ||||||||||||||||
螺筒中部温度 | 227 到 271 | °C | ||||||||||||||||
螺筒前部温度 | 238 到 277 | °C | ||||||||||||||||
射嘴温度 | 249 到 277 | °C | ||||||||||||||||
加工（熔体）温度 | 249 到 277 | °C | ||||||||||||||||
模具温度 | 54.4 到 76.7 | °C | ||||||||||||||||
背压 | 0.345 到 0.689 | MPa | ||||||||||||||||
螺杆转速 | 20 到 100 | rpm | ||||||||||||||||
排气孔深度 | 0.038 到 0.051 | mm | ||||||||||||||||
OTHER PRODUCTS
| 日本旭化成 PPE+PS X1774 Xyron |
| 日本旭化成 POM GT525 |
| AIE PA6 50G3ST物性表 |
| Terlux MABS 2812 HD |
| Polycarbonate (PC) Tarolon 1520 UL黄卡 |
| Polyram PBT PF810物性表 |
| ACRYLITE PLUS PMMA NTA-3 物性表 |
| Epimax PC/ABS311物性表 |
| EVA-三井聚合-210 |
Copyright © sujiaowuxing.com All Rights Reserved，