PEI 1010 物性表资料
PEI材料的其他牌号：
PEI 1000E
PEI 1000
PEI 1000F
PEI 1000P
PEI 1000R
PEI 1010
PEI 1010F
PEI 1000R
加工方法 | · 注射成型 | |||||||||||||||||
多点数据 | · Coefficient of Thermal Expansion vs. Temperature (ASTM E831) · Flexural DMA (ASTM D4065) · Instrumented Impact (Energy) (ASTM D3763) · Instrumented Impact (Load) (ASTM D3763) · Pressure-Volume-Temperature (PVT - Zoller Method) · Shear DMA (ASTM D4065) · Specific Heat vs. Temperature (ASTM D3417) · Tensile Creep (ASTM D2990) · Tensile Fatigue · Tensile Stress vs. Strain (ASTM D638) · Thermal Conductivity vs. Temperature (ASTM E1530) · Viscosity vs. Shear Rate (ASTM D3835) | |||||||||||||||||
物理性能 | 额定值 | 单位制 | 测试方法 | |||||||||||||||
比重 | 1.27 | g/cm3 | ASTM D792 | |||||||||||||||
熔流率 (337°C/6.6 kg) | 18 | g/10 min | ASTM D1238 | |||||||||||||||
收缩率 - 流动 (3.20 mm) | 0.50 到 0.70 | % | Internal Method | |||||||||||||||
吸水率 | ASTM D570 | |||||||||||||||||
24 hr | 0.25 | % | ||||||||||||||||
平衡, 23°C | 1.3 | % | ||||||||||||||||
硬度 | 额定值 | 单位制 | 测试方法 | |||||||||||||||
洛氏硬度 (M 计秤) | 109 | ASTM D785 | ||||||||||||||||
机械性能 | 额定值 | 单位制 | 测试方法 | |||||||||||||||
拉伸模量 3 | 3590 | MPa | ASTM D638 | |||||||||||||||
抗张强度 4 (屈服) | 110 | MPa | ASTM D638 | |||||||||||||||
伸长率 4 | ASTM D638 | |||||||||||||||||
屈服 | 7.0 | % | ||||||||||||||||
断裂 | 60 | % | ||||||||||||||||
弯曲模量 5 (100 mm 跨距) | 3520 | MPa | ASTM D790 | |||||||||||||||
弯曲强度 5 (屈服, 100 mm 跨距) | 165 | MPa | ASTM D790 | |||||||||||||||
抗泰伯磨耗 (1000 Cycles, 1000 g, CS-17 转轮) | 10.0 | mg | ASTM D1044 | |||||||||||||||
冲击性能 | 额定值 | 单位制 | 测试方法 | |||||||||||||||
悬壁梁缺口冲击强度 (23°C) | 32 | J/m | ASTM D256 | |||||||||||||||
无缺口悬臂梁冲击 (23°C) | 1300 | J/m | ASTM D4812 | |||||||||||||||
反向缺口冲击 (3.20 mm) | 1200 | J/m | ASTM D256 | |||||||||||||||
落锤冲击 (23°C) | 33.9 | J | ASTM D3029 | |||||||||||||||
热性能 | 额定值 | 单位制 | 测试方法 | |||||||||||||||
热变形温度 | ASTM D648 | |||||||||||||||||
0.45 MPa, 未退火, 6.40 mm | 207 | °C | ||||||||||||||||
1.8 MPa, 未退火, 6.40 mm | 199 | °C | ||||||||||||||||
维卡软化温度 | 219 | °C | ASTM D1525 6 | |||||||||||||||
线形膨胀系数 - 流动 (-20 到 150°C) | 0.000056 | cm/cm/°C | ASTM E831 | |||||||||||||||
导热系数 | 0.22 | W/m/K | ASTM C177 | |||||||||||||||
RTI Elec | 170 | °C | UL 746 | |||||||||||||||
RTI Imp | 170 | °C | UL 746 | |||||||||||||||
RTI Str | 170 | °C | UL 746 | |||||||||||||||
电气性能 | 额定值 | 单位制 | 测试方法 | |||||||||||||||
体积电阻率 | 1.0E+17 | ohm·cm | ASTM D257 | |||||||||||||||
介电强度 | ASTM D149 | |||||||||||||||||
1.60 mm, in Air | 33 | kV/mm | ||||||||||||||||
1.60 mm, in Oil | 28 | kV/mm | ||||||||||||||||
介电常数 (1 kHz) | 3.15 | ASTM D150 | ||||||||||||||||
耗散因数 | ASTM D150 | |||||||||||||||||
1 kHz | 0.0013 | |||||||||||||||||
2.45 GHz | 0.0025 | |||||||||||||||||
耐电弧性 7 | PLC 5 | ASTM D495 | ||||||||||||||||
相比耐漏电起痕指数(CTI) | PLC 4 | UL 746 | ||||||||||||||||
高电弧燃烧指数(HAI) | PLC 3 | UL 746 | ||||||||||||||||
高电压电弧起痕速率 (HVTR) | PLC 2 | UL 746 | ||||||||||||||||
热丝引燃 (HWI) | PLC 1 | UL 746 | ||||||||||||||||
可燃性 | 额定值 | 单位制 | 测试方法 | |||||||||||||||
UL 阻燃等级 | UL 94 | |||||||||||||||||
0.750 mm | V-0 | |||||||||||||||||
3.00 mm | 5VA | |||||||||||||||||
极限氧指数 | 44 | % | ASTM D2863 | |||||||||||||||
NBS Smoke Density - Flaming, Ds, 4 min | 2.00 | ASTM E662 | ||||||||||||||||
注射 | 额定值 | 单位制 | ||||||||||||||||
干燥温度 | 149 | °C | ||||||||||||||||
干燥时间 | 4.0 到 6.0 | hr | ||||||||||||||||
干燥时间，最大 | 24 | hr | ||||||||||||||||
建议的最大水分含量 | 0.020 | % | ||||||||||||||||
建议注入量 | 40 到 60 | % | ||||||||||||||||
螺筒后部温度 | 332 到 399 | °C | ||||||||||||||||
螺筒中部温度 | 338 到 399 | °C | ||||||||||||||||
螺筒前部温度 | 343 到 399 | °C | ||||||||||||||||
射嘴温度 | 343 到 399 | °C | ||||||||||||||||
加工（熔体）温度 | 349 到 399 | °C | ||||||||||||||||
模具温度 | 135 到 163 | °C | ||||||||||||||||
背压 | 0.345 到 0.689 | MPa | ||||||||||||||||
螺杆转速 | 40 到 70 | rpm | ||||||||||||||||
排气孔深度 | 0.025 到 0.076 | mm | ||||||||||||||||