玻纤增强PPO塑胶原料物性表资料
PPO材料的其他牌号：
AIE PPO 9010-G20 Asia International Enterprise (Hong Kong) Limited PPE+PS
AIE PPO 9010-G30 Asia International Enterprise (Hong Kong) Limited PPE+PS
AIE PPO 9010-SG20 Asia International Enterprise (Hong Kong) Limited PPE+PS
AIE PPO 9010-SG30 Asia International Enterprise (Hong Kong) Limited PPE+PS
Delta PPO 501-FRO Delta Polymers PPE+PS
Delta PPO 844 Delta Polymers PPE+PS
Delta PPO 888 Delta Polymers PPE+PS
Delta PPO FR1-701 Delta Polymers PPE+PS
Delta PPO FR1G21 Delta Polymers PPE+PS
Delta PPO FR1G41 Delta Polymers PPE+PS
加工方法 | · 注射成型 | |||||||||||||||||
物理性能 | 额定值 | 单位制 | 测试方法 | |||||||||||||||
密度 | 1.22 | g/cm3 | ISO 1183 | |||||||||||||||
熔流率 (280°C/5.0 kg) | 5.0 | g/10 min | ISO 1133 | |||||||||||||||
收缩率 | 0.20 到 0.50 | % | ISO 2577 | |||||||||||||||
机械性能 | 额定值 | 单位制 | 测试方法 | |||||||||||||||
拉伸应力 (屈服) | 87.0 | MPa | ISO 527-2/1/50 | |||||||||||||||
弯曲模量 2, 3 | 5500 | MPa | ISO 178 | |||||||||||||||
弯曲强度 2, 3 | 132 | MPa | ISO 178 | |||||||||||||||
冲击性能 | 额定值 | 单位制 | 测试方法 | |||||||||||||||
悬壁梁缺口冲击强度 (23°C) | 12 | kJ/m2 | ISO 180 | |||||||||||||||
热性能 | 额定值 | 单位制 | 测试方法 | |||||||||||||||
热变形温度 | ||||||||||||||||||
0.45 MPa, 未退火, 3.20 mm 跨距 | 155 | °C | ISO 75-2/B | |||||||||||||||
1.8 MPa, 未退火, 3.20 mm 跨距 | 135 | °C | ISO 75-2/A | |||||||||||||||
电气性能 | 额定值 | 单位制 | 测试方法 | |||||||||||||||
表面电阻率 | 1.0E+17 | ohm | IEC 60093 | |||||||||||||||
体积电阻率 | 1.0E+17 | ohm·cm | IEC 60093 | |||||||||||||||
可燃性 | 额定值 | 单位制 | 测试方法 | |||||||||||||||
UL 阻燃等级 | HB | UL 94 | ||||||||||||||||
注射 | 额定值 | 单位制 | ||||||||||||||||
干燥温度 | 100 到 110 | °C | ||||||||||||||||
干燥时间 | 3.0 到 4.0 | hr | ||||||||||||||||
加工（熔体）温度 | 240 到 300 | °C | ||||||||||||||||
模具温度 | 70.0 到 100 | °C | ||||||||||||||||
注塑温度 | 30.0 到 80.0 | MPa | ||||||||||||||||