RheTech Polypropylene FRG130-01 物性表资料

RheTech Polypropylene FRG130-01 物性表资料:聚丙烯(PP)的用途:(1)薄膜制品:聚丙烯薄膜制品透明而有光泽,对水蒸汽和空气的渗透性小,它分为吹膜薄膜、流延薄膜(CPP)、双向拉伸薄膜(BOPP)等2)注塑制品:可用于汽车、电气、机械、仪表、无线电、纺织、国防等工程配件,日用品,周转箱,医疗卫生器材,建筑材料。  3)挤塑制品:可做管材、型材、单丝、渔用绳索。打包带、捆扎绳、编织袋,纤维,复合涂层,片材,板材等。吹塑中空成型制品各种小型容器等。4)其它:低发泡、钙塑板,合成木材,层压板,合成纸,高发泡可作结构泡沫体。PP材料的其他牌号:RheTech Polypropylene F38-01        RheTech, Inc.        PPRheTech Polypropylene F38-04        RheTech, Inc.        PPRheTech Polypropylene F40-01        RheTech, Inc.        PPRheTech Polypropylene F49-01        RheTech, Inc.        PPRheTech Polypropylene F56-01        RheTech, Inc.        PPRheTech Polypropylene FRG130-01        RheTech, Inc.        PPRheTech Polypropylene G10P100-00        RheTech, Inc.        PPRheTech Polypropylene G10P100-01        RheTech, Inc.        PPRheTech Polypropylene G10P100-01UV        RheTech, Inc.        PPRheTech Polypropylene G10UP100-01        RheTech, Inc.        PPRheTech Polypropylene G13P100-00        RheTech, Inc.        PPRheTech Polypropylene G13P100-00UV        RheTech, Inc.        PPRheTech Polypropylene G13P100-01        RheTech, Inc.        PPRheTech Polypropylene G13P100-01UV        RheTech, Inc.        PPRheTech Polypropylene G13P100-332UV        RheTech, Inc.        PP
加工方法 · 注射成型
物理性能
额定值
单位制
测试方法
比重1.42g/cm3ASTM D792
熔流率 (230°C/2.16 kg)4.0g/10 minASTM D1238
硬度
额定值
单位制
测试方法
硬度计硬度 (邵氏 D)78 ASTM D2240
机械性能
额定值
单位制
测试方法
抗张强度 279.3MPaASTM D638
弯曲模量 - 正切7410MPaASTM D790
冲击性能
额定值
单位制
测试方法
悬壁梁缺口冲击强度 (23°C)75J/mASTM D256
落锤冲击0.339JASTM D5420
热性能
额定值
单位制
测试方法
热变形温度 ASTM D648
0.45 MPa, 未退火
158
°C
1.8 MPa, 未退火
147
°C
补充信息
额定值
单位制
测试方法
Reinforcement Content30%ASTM D5630
注射
额定值
单位制
干燥温度51.7 65.6°C
干燥时间1.0 2.0hr
建议的最大水分含量0.050%
螺筒后部温度191 199°C
螺筒中部温度199 210°C
螺筒前部温度199 210°C
射嘴温度204°C
模具温度23.9 35.0°C
注塑温度2.76 8.27MPa
注射速度
保压2.07 6.89MPa
背压0.345 0.689MPa
螺杆转速50 100rpm
合模力2.8 3.4kN/cm2
注射说明
Cycle Time: Variable; Note: Do not leave material in the barrel for extended periods of down time. The flame retardant is temperature sensitive and will degrade when exposed to elevated temperatures for extended periods. Noxious gasses may be evolved.
Drying is Optional
Injection Speed: 0.5 to 1.0 in/min
Purge the machine with polypropylene or polyethylene prior to shut down or change over.
Screw Speed: Slow to Moderate



OTHER PRODUCTS
ExxonMobil LDPE LD 600BA LDPE ExxonMobil Chemical 物性表资料
Alathon M5865PA物性表
Polybutylene/Polyethylene Terephthalate (PBT/PET) GP-7000(g) UL黄卡
Polyamide 66 (PA66) LATAMID 66 H2 G/25 (q) (r) UL黄卡
Polybutylene Terephthalate (PBT) B4406 (o) Q113, B4406 G1 (o) Q113, B4406 G
Polyphenylene Oxide (PPHOX) PX1505(f1)(b), PX1700X(GG)(f1)(b), EN212(f1)(b)
Polystyrene (PS) SEHI-110 UL黄卡
Ultradur B 4300 G4 LS High Speed BLK 15045物性表
Udel PSU P-3700 HC 物性表
Copyright © sujiaowuxing.com All Rights Reserved,