Endura FSPP-211 物性表资料

加工方法

· 注射成型

比重

1.37

g/cm3

ASTM D792

熔流率 (230°C/2.16 kg)

4.0

g/10 min

ASTM D1238

收缩率 - 流动

1.0

%

ASTM D955

硬度计硬度 (邵氏 D)

77

ASTM D2240

抗张强度 (屈服)

16.9

MPa

ASTM D638

伸长率 (断裂)

15

%

ASTM D638

弯曲模量

1930

MPa

ASTM D790

弯曲强度

32.8

MPa

ASTM D790

悬壁梁缺口冲击强度

43

J/m

ASTM D256

热变形温度 (1.8 MPa, 未退火)

54.4

°C

ASTM D648

最高连续使用温度

105

°C

ASTM D794

维卡软化温度

141

°C

ASTM D1525

体积电阻率

1.8E+16

ohm·cm

ASTM D257

介电强度

32

kV/mm

ASTM D149

介电常数 (1.00 GHz)

2.64

ASTM D150

耗散因数 (1.00 GHz)

0.0027

ASTM D150

耐电弧性 (3.18 mm)

76.0

sec

ASTM D495

UL 阻燃等级 (1.47 mm, All Colors)

V-0

UL 94

极限氧指数 (3.18 mm)

28

%

ASTM D2863

The value listed as Max. Continuous Use Temp, ASTM D794, was tested in accordance with UL-746B.
Dielectric Strength, ASTM D 149, moist: 814V/mil
Volume Resistivity, ASTM D 150, moist: 26.4e10
High-Current Arc Resistance, UL-746, Arcs to Ignite, On Surface, 0.058in: No Ignition
High-Current Arc Resistance, UL-746, Arcs to Ignite, On Surface, 0.125in: No Ignition
High-Current Arc Resistance, UL-746, Arcs to Ignite, 1/16 in. above surface, 0.058in: No Ignition
High-Current Arc Resistance, UL-746, Arcs to Ignite, 1/16 in. above surface, 0.125in: No Ignition
High-Current Arc Resistance, UL-746, Arcs to Ignite, 1/4 in. above surface, 0.058in: No Ignition
High-Current Arc Resistance, UL-746, Arcs to Ignite, 1/4 in. above surface, 0.125in: No Ignition
Hot Wire Ignition, UL 746, Seconds to ignite, 0.058in: No Ignition
Hot Wire Ignition, UL 746, Seconds to ignite, 0.125in: No Ignition
Arc Tracking Ratio, UL 746, inches per minute, 0.058in: 0
Arc Tracking Ratio, UL 746, inches per minute, 0.125in: 0
High-Voltage Arc Resistance, UL 746, Seconds to track, 0.058in: No Track
High-Voltage Arc Resistance, UL 746, Seconds to track, 0.1.25in: No Track
High-Voltage Arc Resistance, UL 746, Seconds to ignite, 0.058in: No Ignition
High-Voltage Arc Resistance, UL 746, Seconds to ignite, 0.1.25in: No Ignition