ABS-日本东丽-700

原料描述规格级别：高抗冲级外观颜色：---用途概述：---备注说明：--- 原料技术性能项目试验条件[状态]测试方法测试数据数据单位物理性能比重23℃ASTM D-7921.05--- 吸水性23℃×24hrsASTM D-5700.3% 熔体流动速率220℃ 10kgISO-113323g/10min 模塑收缩率---ASTM D-9550.4-0.6% 表面阻力23℃ASTM D-257＞1016ohm 体积阻力23℃ASTM D-257＞1016ohm.cm 阻燃性---UL-94HB--- 机械性能IZOD冲击强度12.7×62.5×12.7mm12.7×62.5×3.2mm23℃23℃ASTM D-256ASTM D-25619(186)20(196)kg.cm/cm(J/m)kg.cm/cm(J/m)IZOD冲击强度12.7×62.5×12.7mm12.7×62.5×3.2mm0℃0℃ASTM D-256ASTM D-25611(108)16(157)kg.cm/cm(J/m)kg.cm/cm(J/m)IZOD冲击强度12.7×62.5×12.7mm12.7×62.5×3.2mm-30℃-30℃ASTM D-256ASTM D-2568(78)12(118)kg.cm/cm(J/m)kg.cm/cm(J/m)洛氏硬度---ASTM D-785115R 拉伸强度23℃(strainrate:5%)ASTM D-638510(50)kg/cm(MPa) 拉伸断裂伸长率23℃ASTM D-63835% 弯曲强度23℃(strainrate:3%)ASTM D-790770(76)kg/cm(MPa) 弯曲模量23℃ASTM D-79025000(2450)kg/cm(MPa) 电气性能绝缘强度Short timeASTM D-19423KV/mm 介电常数1000HzASTM D-1503.1--- 电力因数1000HzASTM D-1506.1×10-3--- 热 性 能热传导性能---ASTM C1770.15W/K.m 热变形温度127×12.7×12.7mm127×12.7×6.4mm18.56kg/cm18.56kg/cmASTM D-648ASTM D-6489287℃℃线性膨胀系数---ASTM D-6967.1×10-5mm/mm℃