RTP ABS+PC 2587

RTP ABS+PC 2587

产品名称：RTP ABS+PC 2587. 当 前 价：面议. 最小起订：25kg. . . . RTP ABS+PC 2587 RTP ABS+PC 2587-详细说明: 　　 　　
RTP 2587 ABS+PC RTP Company

特性：40%碳纤维增强材料加工方法：注射成型供应 RTP 2587 ABS+PC 型号如下：

RTP 2587 ABS+PC RTP Company
RTP 2500 A HB ABS+PC RTP Company
RTP 2500 A TFE 10 UV ABS+PC RTP Company
RTP 2500 A TFE 10 ABS+PC RTP Company
RTP 2500 A TFE 15 ABS+PC RTP Company
RTP 2500 A TFE 5 ABS+PC RTP Company
RTP 2500 A ABS+PC RTP Company
RTP 2500 FR A ABS+PC RTP Company
RTP 2500 FR-110 ABS+PC RTP Company
RTP 2500 FR-3010 ABS+PC RTP Company
RTP 2500 HF A ABS+PC RTP Company
RTP 2500 TFE 10 ABS+PC RTP Company
RTP 2500 TFE 15 FR ABS+PC RTP Company
RTP 2500 TFE 20 FR ABS+PC RTP Company
RTP 2500 TFE 5 ABS+PC RTP Company
RTP 2500 UV ABS+PC RTP Company
RTP 2500.5 ABS+PC RTP Company
RTP 2500 ABS+PC RTP Company
RTP 2501 A ABS+PC RTP Company
RTP 2501 FR ABS+PC RTP Company
RTP ABS+PC 2587 物性表：

物理性能	额定值	单位制	测试方法
比重	1.34	g/cm³	ASTMD792
收缩率 - 流动 (3.20 mm)	0.050 到 0.20	%	ASTMD955
含水量	0.020	%

机械性能	额定值	单位制	测试方法
拉伸模量	16500	MPa	ASTMD638
抗张强度	159	MPa	ASTMD638
伸长率 (屈服)	0.50 到 1.5	%	ASTMD638
弯曲模量	15900	MPa	ASTMD790
弯曲强度	214	MPa	ASTMD790
冲击性能	额定值	单位制	测试方法
悬壁梁缺口冲击强度 (3.20 mm)	64	J/m	ASTMD256
无缺口悬臂梁冲击 (3.20 mm)	370	J/m	ASTMD256

电气性能	额定值	单位制	测试方法
表面电阻率 2	< 1.0E+2	ohm	ASTMD257
体积电阻率	< 1.0	ohm·cm	ASTMD257
Static Decay	< 0.5	sec	FTMS 101C4046.1

补充信息	额定值	单位制
Primary Additive	40	%

注射	额定值	单位制
干燥温度	93.3	°C
干燥时间	4.0	hr
Dew Point	-28.9	°C
加工（熔体）温度	243 到 274	°C
模具温度	51.7 到 93.3	°C
注塑温度	68.9 到 103	MPa

随货提供 RTP ABS+PC 2587 原厂物理性能表,UL黄,COC,SGS等资料！

--

RTP ABS+PC 2587 合金：

是高抗冲击，无定形聚碳酸脂（PC）与丙烯腈-丁二烯-苯乙烯三元共聚物（ABS）的共混物。它具备PC的耐冲击性和忧良的耐碳性，及ABS的高流动性。 可以被定制，来满足特殊的性能要求，以获得性能，成本，可加工性的最佳平衡，应用于汽车车身壁板和仪表板，计算机外壳，移动电话，家电用品，照明设备等。
　



RTP ABS+PC 2587