DOW Wire & Cable DFDA-1254 NT 物性表资料

DOW Wire & Cable DFDA-1254 NT 物性表资料
低密度聚乙烯(LDPE)的应用:
LDPE适合热塑性成型加工的各种成型工艺,成型加工性好,如注塑,挤塑,吹塑,旋转成型,涂覆,发泡工艺,热成型,热封焊,热焊接等。
LDPE材料的其他牌号
DOW LDPE PG 7014 LDPE Dow Plastics
DOW LDPE PT 7007 LDPE Dow Plastics
DOW LDPE PT 7009 LDPE  Dow Plastics
DOW Wire & Cable DFD-4960 NT LDPE Dow Plastics
DOW Wire & Cable DFDA-1253 NT LDPE Dow Plastics
DOW Wire & Cable DFDA-1254 NT LDPE Dow Plastics
DOW Wire & Cable DFD-4960 NTm LDPE Dow Plastics
DOW Wire & Cable DFDA-1253 NT Dow Plastics
DOW Wire & Cable DFDA-1254 NT Dow Plastics
DOW Wire & Cable DFDD-0588 BK Dow Plastics
DOW Wire & Cable DFDL-0588 BK Dow Plastics
DOW Wire & Cable DFNA-0012 NT Dow Plastics
DOW Wire & Cable DFNA-0078 NT Dow Plastics
物理性能
额定值
单位制
测试方法
比重
0.918
g/cm3
ASTM D792
熔流率 (190°C/2.16 kg)
8.0
g/10 min
ASTM D1238
机械性能
额定值
单位制
测试方法
抗张强度
9.65
MPa
ASTM D638
伸长率 (断裂)
500
%
ASTM D638
电气性能
额定值
单位制
测试方法
体积电阻率
> 1.0E+17
ohm·cm
ASTM D257
介电强度 2 (3.18 mm)
43
kV/mm
ASTM D149
Dielectric Constant
ASTM D1531
1 MHz
2.29
2.47 GHz
2.27
耗散因数
ASTM D1531
1 MHz
0.00010
2.47 GHz
0.00030
挤出
额定值
单位制
熔体温度
170 200
°C
挤压说明
DFDA-1254 NT provides excellent surface finish and outstanding output rates over a broad range of conditions. For optimum results, use melt extrusion temperatures in the suggested range of 338 to 392°F (170-200°C). However, specific recommendations for processing conditions can be determined only when the application and type of processing equipment are known. Please contact your local Dow Chemical Wire and Cable Sales Representative for such particulars.



OTHER PRODUCTS
PP EC440P Clyrell
沙特SABIC LLDPE MG200024
台湾长春 电木粉 T375HF
VICOTE PEEK 701物性表
Acrylic Polymer No.5511S UL黄卡
Acetal "Polyoxymethylene" (POM) ES-5(r4) UL黄卡
(Styrene Ethylene Butylene Styrene/Polypropylene/Polyurethane (SEBS/PP/PUR) 
Polyamide 66 (PA66) Radilon-A USX 200(a) UL黄卡
CYCOLOY pc/ABS MC8100 Resin物性表
Copyright © sujiaowuxing.com All Rights Reserved,