J-REX LD JH526N 物性表资料
低密度聚乙烯（LDPE）的应用：
LDPE复合挤压广泛作为高阻隔复合层压板的一种组分。重要的要求就是防湿和密封。满足不同的要求，树脂的性能随之不同。它可用于无菌包装、药品与日用品的包装。LDPE主要用途用于薄膜产品（如农业用薄膜，地面覆盖膜，农膜，蔬菜大棚膜，）包装用膜（如糖果，蔬菜，冷冻食品等膜，液体包装用如吹塑薄膜，重包装袋，收缩包装袋，一般工业包装薄膜和食品袋等，还可用于注塑产品；挤塑管材，电线电缆，吹塑中空容器。
LDPE材料的其他牌号：
J-REX LD JF324S LDPE Japan Polyolefins Co., Ltd.
J-REX LD JF3305 LDPE Japan Polyolefins Co., Ltd.
J-REX LD JF330N LDPE Japan Polyolefins Co., Ltd.
J-REX LD JF424S LDPE Japan Polyolefins Co., Ltd.
J-REX LD JF430N LDPE Japan Polyolefins Co., Ltd.
J-REX LD JF430S LDPE Japan Polyolefins Co., Ltd.
J-REX LD JF430T LDPE Japan Polyolefins Co., Ltd.
J-REX LD JF436A LDPE Japan Polyolefins Co., Ltd.
J-REX LD JF454S LDPE Japan Polyolefins Co., Ltd.
J-REX LD JF524S LDPE Japan Polyolefins Co., Ltd.
J-REX LD JF530S LDPE Japan Polyolefins Co., Ltd.
J-REX LD JF536A LDPE Japan Polyolefins Co., Ltd.
J-REX LD JF630S LDPE Japan Polyolefins Co., Ltd.
J-REX LD JF635S LDPE Japan Polyolefins Co., Ltd.
J-REX LD JH455N LDPE Japan Polyolefins Co., Ltd.
J-REX LD JH507C LDPE Japan Polyolefins Co., Ltd.
J-REX LD JH526N LDPE Japan Polyolefins Co., Ltd.
加工方法 | · 挤压层涂法 | |||||||||||
物理性能 | 额定值 | 单位制 | 测试方法 | |||||||||
比重 | 0.923 | g/cm3 | ASTM D792 | |||||||||
熔流率 (190°C/2.16 kg) | 3.5 | g/10 min | ASTM D1238 | |||||||||
硬度 | 额定值 | 单位制 | 测试方法 | |||||||||
硬度计硬度 (邵氏 D) | 54 | ASTM D2240 | ||||||||||
机械性能 | 额定值 | 单位制 | 测试方法 | |||||||||
抗张强度 | ASTM D638 | |||||||||||
屈服 | 10.0 | MPa | ||||||||||
断裂 | 14.0 | MPa | ||||||||||
伸长率 (断裂) | 580 | % | ASTM D638 | |||||||||
弯曲强度 (屈服) | 150 | MPa | ASTM D790 | |||||||||
热性能 | 额定值 | 单位制 | 测试方法 | |||||||||
脆化温度 | -70.0 | °C | ASTM D746 | |||||||||
维卡软化温度 | 96.0 | °C | ASTM D1525 | |||||||||
熔融温度 | 111 | °C | DSC | |||||||||
补充信息 | ||||||||||||
Most properties were tested in accordance with JIS test standards | ||||||||||||