J-REX LD JH536N 物性表资料
低密度聚乙烯（LDPE）的应用：
LDPE适合热塑性成型加工的各种成型工艺，成型加工性好，如注塑，挤塑，吹塑，旋转成型，涂覆，发泡工艺，热成型，热封焊，热焊接等。
LDPE材料的其他牌号：
J-REX LD JH527N LDPE Japan Polyolefins Co., Ltd.
J-REX LD JH536N LDPE Japan Polyolefins Co., Ltd.
J-REX LD JH606N LDPE Japan Polyolefins Co., Ltd.
J-REX LD JH607C LDPE Japan Polyolefins Co., Ltd.
J-REX LD JH707N LDPE Japan Polyolefins Co., Ltd.
J-REX LD JH778K LDPE Japan Polyolefins Co., Ltd.
J-REX LD JK121A LDPE Japan Polyolefins Co., Ltd.
J-REX LD JK268A LDPE Japan Polyolefins Co., Ltd.
J-REX LD JK311A LDPE Japan Polyolefins Co., Ltd.
J-REX LD JK401N LDPE Japan Polyolefins Co., Ltd.
J-REX LD JM314A (Blow Molding)LDPE Japan Polyolefins Co., Ltd.
J-REX LD JM314A (Injection Molding) LDPE Japan Polyolefins Co., Ltd.
加工方法 | · 挤压层涂法 | |||||||||||
物理性能 | 额定值 | 单位制 | 测试方法 | |||||||||
比重 | 0.924 | g/cm3 | ASTM D792 | |||||||||
熔流率 (190°C/2.16 kg) | 3.5 | g/10 min | ASTM D1238 | |||||||||
硬度 | 额定值 | 单位制 | 测试方法 | |||||||||
硬度计硬度 (邵氏 D) | 55 | ASTM D2240 | ||||||||||
机械性能 | 额定值 | 单位制 | 测试方法 | |||||||||
抗张强度 | ASTM D638 | |||||||||||
屈服 | 11.0 | MPa | ||||||||||
断裂 | 14.0 | MPa | ||||||||||
伸长率 (断裂) | 580 | % | ASTM D638 | |||||||||
弯曲强度 (屈服) | 160 | MPa | ASTM D790 | |||||||||
热性能 | 额定值 | 单位制 | 测试方法 | |||||||||
脆化温度 | -70.0 | °C | ASTM D746 | |||||||||
维卡软化温度 | 98.0 | °C | ASTM D1525 | |||||||||
熔融温度 | 112 | °C | DSC | |||||||||
补充信息 | ||||||||||||
Most properties were tested in accordance with JIS test standards | ||||||||||||