加工方法 | · 挤压层涂法 | |||||||||||||
物理性能 | 额定值 | 单位制 | 测试方法 | |||||||||||
密度 | 0.918 | g/cm3 | ASTM D1505 | |||||||||||
熔流率 (190°C/2.16 kg) | 14 | g/10 min | ASTM D1238 | |||||||||||
硬度 | 额定值 | 单位制 | 测试方法 | |||||||||||
硬度计硬度 (邵氏 D) | 50 | ASTM D2240 | ||||||||||||
机械性能 | 额定值 | 单位制 | 测试方法 | |||||||||||
抗张强度 | 11.0 | MPa | ASTM D638 | |||||||||||
伸长率 (屈服) | 500 | % | ASTM D638 | |||||||||||
弯曲强度 | 207 | MPa | ASTM D790 | |||||||||||
热性能 | 额定值 | 单位制 | 测试方法 | |||||||||||
维卡软化温度 | 28.9 | °C | ASTM D1525 | |||||||||||
挤出 | 额定值 | 单位制 | ||||||||||||
熔体温度 | 310 到 327 | °C | ||||||||||||
挤压说明 | ||||||||||||||
It is recommended that a melt temperature of 590 - 620°F be used for light-weight coating applications in conjunction with electrostatic, flame or chemical priming to insure good adhesion. The maximum recommended melt temperature for LD-13.5-918 is 625°F. |