低密度聚乙烯（LDPE）的应用：

LDPE适合热塑性成型加工的各种成型工艺，成型加工性好，如注塑，挤塑，吹塑，旋转成型，涂覆，发泡工艺，热成型，热封焊，热焊接等。

LDPE材料的其他牌号：

Petrothene NA960000 LDPE LyondellBasell Industries

Petrothene NA960070 LDPE LyondellBasell Industries

Petrothene NA960083 LDPE LyondellBasell Industries

Petrothene NA963 LDPE LyondellBasell Industries

Petrothene NA963046 LDPE LyondellBasell Industries

Petrothene NA963083 LDPE LyondellBasell Industries

Petrothene NA967000 LDPE LyondellBasell Industries

Petrothene NA980 LDPE LyondellBasell Industries

Petrothene NA980000 LDPE LyondellBasell Industries

Petrothene NA983085 LDPE LyondellBasell Industries

Petrothene NA985 LDPE LyondellBasell Industries

Petrothene NA985107 LDPE LyondellBasell Industries

Petrothene NA985132 LDPE LyondellBasell Industries

Petrothene PM92973 LLDPE LyondellBasell Industries

Petrothene YR92866 LDPE+EVA LyondellBasell Industries

Plastiblend LDPE E FR V-2 LDPETP Composites, Inc.

Plexar PX1775 LDPE LyondellBasell Industries

加工方法		· 薄膜挤出
物理性能	额定值		单位制	测试方法
密度	0.920		g/cm3	ASTM D1505
熔流率 (190°C/2.16 kg)	1.0		g/10 min	ASTM D1238
机械性能	额定值		单位制	测试方法
抗张强度 2 (1.91 mm)	14.5		MPa	ASTM D638
伸长率 (断裂)	660		%	ASTM D638
薄膜	额定值		单位制	测试方法
薄膜厚度 - 经测试	32		μm
割线模量				ASTM D882
MD: 吹塑薄膜	200		MPa
TD: 吹塑薄膜	234		MPa
抗张强度				ASTM D882
MD: 屈服, 32 μm, 吹塑薄膜	24.1		MPa
TD: 屈服, 32 μm, 吹塑薄膜	16.5		MPa
伸长率				ASTM D882
MD: 断裂, 32 μm, 吹塑薄膜	200		%
TD: 断裂, 32 μm, 吹塑薄膜	500		%
落锤冲击 (32 μm, 吹塑薄膜)	120		g	ASTM D1709
埃尔曼多夫抗撕强度				ASTM D1922
MD: 32 μm, 吹塑薄膜	300		g
TD: 32 μm, 吹塑薄膜	130		g
热性能	额定值		单位制	测试方法
维卡软化温度	92.0		°C	ASTM D1525
补充信息
Film data obtained from film produced in a 3 1/2" (89 mm) blown film line, commercially available 8" (203 mm) die, 350°F (177°C) melt extrusion temperature, 2:1 BUR, 1.25 mil (32 micron) gauge, 0.025" die gap at 150 lb/hr.