XLPE ATP/130-XU物性表资料

加工方法

密度

0.948

g/cm3

ISO 1183

熔流率 (190°C/5.0 kg)

1.8

g/10 min

ASTM D1238

硬度计硬度 (邵氏 D)

60

ASTM D2240

拉伸应力 (屈服)

24.0

MPa

ISO 527-2

拉伸应变 (断裂)

370

%

ISO 527-2

维卡软化温度

123

°C

ISO 306

溶融温度（DSC）

135

°C

ISO 3146

· Reaction between grafting and catalyst, must be mixed before starting extrusion in the ratio, Grafting/Catalyst: 95/5
Compression Set, 1000h, 4.4 Mpa, 95°C: pass
Compression Set, 1h, 4.8 Mpa, 95°C: pass
Melt Flow Rate, ASTM D1238, 190°C/5 kg: 0.5 to 3 g/10min
Crosslinking of the finished product is obtained by:
Immersion of the bobbin in hot water at 85/90°C for two hours up to 3 mm thickness

· Steam treatment at 0.15 bar for 5/6 hours

Reaction between grafting and catalyst, must be mixed before starting extrusion in the ratio, Grafting/Catalyst: 95/50
Compression Set, 1000h, 4.4 Mpa, 95°C: pass

第1气缸区温度

170

°C

第2气缸区温度

175

°C

第3气缸区温度

180

°C

第4气缸区温度

190

°C

第5气缸区温度

200

°C

模具温度

220

°C

· The extrusion parameters listed are for 18 mm pipe.
22 mm pipe:
Zone 1 Temperature: 175°C

· Zone 2 Temperature: 180°C

· Zone 3 Temperature: 185°C

· Zone 4 Temperature: 195°C

· Head Temperature: 210°C

· Die Temperature: 215 to 225°C